Material Sealing tipe kering SDM 100 adalah material sealing epoksi dengan kinerja tinggi untuk pemeliharaan serta penguatan bangunan gedung. Material ini digunakan di banyak sisi seperti di bagian sambungan, retak, penutupan lubang pin, alat injeksi bangunan dari bangunan beton seperti jembatan, DAM, terowongan, kereta bawah tanah, apartemen, dll dan bahan ini memiliki kekuatan rekat yang sangat baik.
The intended use
01
Connecting parts of PC (pre-cast) slabs from concrete buildings
Connecting and closing parts that are strengthened from iron plates
05
Connecting soundproof walls from precast concrete
06
Connect the joints of the assembled culvert
07
Connecting road boundaries
08
Another multi-purpose sealing job
Characteristics
01
Excellent mixing and usability due to its paste characteristics
02
Strong adhesion, tension, pressure and bending strength, and good impact resistance.
03
Extraordinary physical strength and easy to move
04
No shrinkage
05
Excellent durability and adhesion and also waterproof
06
Good resistance to alkali, salt, and acid.
General Specifications
01
Specification
Classification
Resin
Hardener
Main component
Epoxy Resin
Polyamide Amin
Outer Appearance
White
Ashes
Mix Ratio (Weight Ratio)
Resin : Hardener = 1 : 1
Mixing Specific Gravity (25℃)
50 ± 10 minutes (based on mixing 100g)
Pot Life Table (25℃)
4 ± 1 jam
Hardening Time (25℃)
24 ~ 36 jam
Theoretical Amount Required
Glue injector for crack repair work 0.2kg/m, compressed iron plate 0.6~0.7 kg/㎡
02
Nature
Test Name
Unit
Mold Value
Information
Non Volatile Material
%
Over 95.0
Dry Layer Condition
-
Normal
Durometer Hardness
Shore D
Over 80
Stress Strength
N/㎟
Over 65
Adhesive Strength
N/㎟
More than 7
03
Packaging Unit: Resin = 10kg, Hardener = 10kg
04
Storage Time: 12 months (avoid direct sunlight)
Method of use
01
Mix the resin and hardener for 2~3 minutes by measuring according to the predetermined mixing ratio. (The desired material specifications cannot be obtained if the ratio and mixing process are not followed as per the stated regulations.)
02
Only use the material during the pot life because the material will harden when heated and the material will also cause chemical reactions after the pot life has expired after being mixed. (The higher the temperature, the faster the pot life, pot life and hardening may be slower during winter or at low temperatures.)
03
Mixing of products must be carried out near the construction (work) site.
Terms of Work
01
The temperature of the coating surface should be more than 5℃ and to avoid condensation of water components, the surface should be higher than the dew point of 3℃ and should be 80% lower than the relative humidity.
Attention
01
Avoid application if the temperature is below 5℃ or at the dew point.
02
Immediately wash the equipment with the specified cleaning product immediately after use.
03
The remaining product is stored sealed in an unexposed place and do not let children touch with their hands.
04
When swallowed or in contact with skin, please take the actions listed on the Material Safety Data Sheet (MSDS) and immediately consult a specialist.
English
Korea
INA